Tên tài liệu/ đề tài, dự án: PbS-sensitized K2Ti4O9 composite: Preparation and photocatalytic properties for hydrogen evolution under visible light irradiation
Tác giả/ chủ nhiệm: Wenquan Cui, Shanshan Ma, Li Liu, Yinghua Liang
Năm xuất bản: 2012
Thời gian đăng: 04/08/2015
Danh mục: Tập 204 - 206
File đính kèm:
Thông tin mô tả:

PbS-sensitized K2Ti4O9 composite photo-catalysts (hereafter designated as PbS/K2Ti4O9) were prepared by a facile deposition–precipitation method. The samples were characterized by scanning electron microscopy (SEM), energy dispersive X-ray (EDS), X-ray diffraction (XRD), ultraviolet–visible diffuse reflectance spectra (UV–Vis DRS), X-ray photoelectron spectroscopy (XPS) and photoluminescence measurement (PL). The photo-catalytic activities were investigated under visible light irradiation. The results indicated that the size of PbS, which uniformly scattered on the surface of K2Ti4O9, distribute in the range of 50–100 nm. The absorption edge of K2Ti4O9 shifted to the visible light region and recombination of electrons and holes was suppressed after the deposition of PbS. The composite photo-catalyst loading 25 wt.% PbS synthesized by deposition–precipitation method showed the highest photo-catalytic activity. The amount of hydrogen evolution is 1.85 mmol/g after 3 h irradiation over 0.5 g catalyst in the reaction system containing Na2S– Na2SO3–KOH aqueous solution. Finally, the mechanism of the photo-catalysis was discussed.

Từ khóa tìm kiếm: PbS, K2Ti4O9, Deposition–precipitation, Photo-catalysis, Hydrogen evolution